Karakterisasi dan Aplikasi Katalis Nikel-Molibdenum Teremban pada Zeolit Alam Aktif untuk Hidrorengkah Tir Batubara
Abstract
Preparation and characterization of nickel-molybdenum catalysts supported on activated natural zeolite over hydrorackingof coal tar have been done. Modification of catalyst was included activation of zeolite by HCl 6N, wet impregnation of Ni-Mo metal and leaching the Ni-Mo from zeolite surfaces with EDTA solution.The parameters of catalyst have been determinedi.e acid site number, the ratio of Si/Al, crystallinity, content of Ni-Mo metal, specific surface area, total pore volume, and poreaverage diameter. The hydrocracking of coal tar was carried out at the optimum temperature (450°C) by flowing H2 gas (flowrate of 20 mL/min) on the coal tar with ratio of feed:catalyst was 10:1. The resulting liquid product was analyzed by GC/GCMS.The result showed that catalytic hydrocracking with ZAA catalyst had the highest conversion of liquid products,which were 40.51% (w/w) compared to Ni-Mo/ZAA catalyst gave 28.61% and Ni-Mo/ZAA(E) gaves 28.06% (w/w). Thehighest light fractions (67.63% (w/w)) produced by using Ni-Mo/ZAA catalyst and the highest medium fractions wereproduced over ZAA catalyst which was 36.61% (w/w) and the highest total conversion on the product with Ni-Mo/ZAA(E)catalyst produced was 50.05% (w/w). The product analyzed with GC-MS result on the 9th highest peak showed that thehydrocracking products resulted over Ni-Mo/ZAA mostly were phenol and its derivatives.
Keywords
Full Text:
PDFReferences
Amin, S.J., Nikooee, E., Ghatee.,Ayatollahi, S.H.,Alamdai, A & Sedghamiz, T. 2011. Investigating the effect of different asphaltene structures on surface topography and wettability alteration. Appl. Surf. Sci 257: 8341– 8349.
Benhabib, K., Faure, P., Sardin, M & Simonnot, M.O. 2010. Characteristics of a solid coal tar sampled from a contaminated soil and of the organics transferred into water. J. Fuel 89: 352–359.
Eberly, E.P, Jr., Kimberlin, N.C., Miller, H.W & Drushel, V.H. 1966. Coke formation on silica-alumina cracking catalyst. Ind. Eng. Chem. Process Des. Dev 5: 193– 197.
, D., Hutchitson, J & Li, L. 1990. An analysis of factor that influence shape selectivity in the cracking of long-chain alkanes on zeolites catalyst. J. Catal 122: 34–43.
Heraldy, E., Hisyam, S.W & Sulistiyono . 2003. Characterization and Activation of Natural Zeolite From Ponorogo. Indo. J. Chem 3: 91–97.
Jiang, J., Wang, Q., Wang, Y., Tong, W & Xiao, B. 2007. GC/MS analysis of coal tar composition produced from coal pyrolysis. Bull. Chem. Soc. Ethiop 21: 229–240.
Lestari, Y.D. 2010. Kajian modifikasi dan karakterisasi zeolit dari berbagai negara. Profesionalisme peneliti dan pendidik dalam riset dan pembelajaran yang berkualitas dan berkarakter. Proseding Nasional Kimia dan Pendidikan Kimia. Yogyakarta, 30 Oktober 2010.
Li, G. 2005. FT-IR studies of zeolite material : Characterization and environmental applications, Dissertation, Mathematic and Natural Science Faculty. Iowa: University of Iowa.
Nasikin, M & Susanto, H, B. 2010. Katalisis heterogen. Jakarta: UI–Press.
Pavia, D.L., Lampman, M.G., Kriz, S.G& Vyvyan, R.J. 2009. Introduction to spectroscopy, 4th. Sidney: Brooks/Cole.
Rachmat, A. 2001. Pengaruh temperatur pirolisis dan jenis pelarut pada ektraksi terhadap produk cair batubara peringkat rendah. Tesis Pasasarjana. Fakultas Matematika dan Ilmu Pengetahuan Alam. Yogyakarta: Universitas Gadjah Mada.
Raseev, S. 2003. Thermal and catalytic processes in petroleum refining. New York: Marcel Dekker, Inc. 681– 694.
Richardson, S.M, Nagaishi, H & Graym M.R. 1996. Initial coke deposition on a NiMo/ã-Al2O3 bitumen hydroprocessing catalyst. Ind. Eng. Chem. Res 35:
–3950.
Saerodji, G.M. 2013. Preparasi, karakterisasi dan uji aktivitas katalis logam Ni, Co, NiMo, dan CoMo yang diembankan pada zeolit alam aktif untuk hidrorengkah plastik polietilena menjadi fraksi bensin dan diesel. Skripsi Sarjana. Fakultas Matematika dan Ilmu Pengetahuan Alam. Yogyakarta: Universitas Gadjah Mada.
Simseek, B,E., Ozdemir, E & Beker, U. 2013. Zeolite supported mono- and bimetallicoxides: Promising adsorbents for removal of As (V) in aqeous solutions. J. Chem. Eng 220: 02–411.
Trisunaryanti, W., Triwahyuni, E & Sudiono, S. 2005. Preparasi, modifikasi dan karakterisasi katalis Ni-Mo/ zeolit alam dan Mo-Ni/zeolit alam. J. Teknoin 10: 269– 282.
Usui, K., Kidena, K., Murata, S., Nomura, M & Trisunaryanti, W. 2004. Catalytic Hydrocracking of petroleum derived asphaltenes by transition metal-loaded zeolite catalysts J. Fuel 83: 1899-1906
DOI: http://dx.doi.org/10.31258/jnat.16.1.10-22
Refbacks
- There are currently no refbacks.
Copyright (c) 2015 Dwi Julian Sugianto, Karna Wijaya, Iqmal Tahir
This work is licensed under a Creative Commons Attribution 4.0 International License.